For a reliable seal on your aircraft's most critical components, order PPG Aerospace® PR-1425CF Windshield and Canopy Sealant from SkyGeek. Sold in a. 6-ounce 654-SemKit, the sealant is easy to apply with a smooth bead that ensures a better seal. The chrome-free formula offers an accelerated cure time and is the ideal choice for windshield repairs and replacement. PPG Aerospace® PR-1425CF Windshield and Canopy Sealant has a service temperature range from -65°F(-54°C) to 250°F (121°C) and can withstand brief exposure to temperatures up to 275°F (135°C). PPG Aerospace® PR-1425CF Windshield and Canopy Sealant is compatible with glass, polycarbonate and acrylic substrates. When applied to a properly prepared surface, the sealant will not craze substrates. Once cured, PPG Aerospace® PR-1425CF Windshield and Canopy Sealant exhibits excellent resistance to UV and weather exposure.
PPG Aerospace® PR-1425CF Windshield and Canopy Sealant from SkyGeek is a Class B, fast-curing polysulfide compound. Uncured, the sealant is a low sag, thixotropic paste that can easily be applied directly from the SemKit that it is packaged in. Use PPG Aerospace PR-1861 adhesion promoter to ensure a strong bond and reliable seal.
| Application Properties (typical) | | | Color | Part A - Black
Part B - Black
Mixed - Black | | Mixing ratio by weight | Part A: Part B
10:100 | | Base Viscosity | 16,000, (1600)
(Brookfield #6 @ 10rpm), Poise (Pa-s) | Application life and cure time
@ 77°F (25°C), 50% RH | | | Application life (hours) | Tack free time (hours) | Cure time to 35 A Durometer (hours) | | B-1/2 | 1/2 | <8 | 24 | | B-1 | 1 | <24 | 48 | | B-2 | 2 | <24 | 48 | | |
| Performance Properties (typical) | | | Cure Time | 7 days @ 77°F (25°C), 50% RH | | Cured specific gravity | 1.49 | | Nonvolatile content,(%) | 93% | | Ultimate cure hardness (Durometer A) | 55 | | Peel strength, pli (N/25 mm),100% cohesion | | Dry, 14 days @ 77°F (25°C) | | MIL-G-25667 (Glass) - 50 (222) | | MIL-P-8184 (Acrylic)* - 48 (214) | | MIL-P-83310 (Polycarbonate)* - 46 (205) | | MIL-S-5059 (Stainless steel)* - 46 (205) | | MIL-T-9046 (Titanium comp. C)* - 46 (205) | | QQ-A-250/12 (Aluminum) - 46 (205) | | *Primed with PR-142 Adhesion Promoter | | | Thermal rupture resistance | Retains pressure of 10 psi with only negligible deformation, both before and after immersion in JRF. | | Low temperature flexibility @ -65°F (-54°C) | No cracking, checking or loss of adhesion. | | Corrosion resistance | No corrosion, adhesion loss, softening, or blistering after 20-day immersion in 2-layer salt water/JRF @ 140°F (60°C). | | Resistance to fluids | Excellent resistance to water, alcohols, petroleum-base and synthetic lubricating oils, and petroleum-base hydraulic fluids. | | Flexibility | No cracks after bending 180 degrees over 0.125 inch (3.18 mm) mandrel. | | Repairability to itself | Excellent to both freshly cured as well as fuel aged and abraded fillets. | | Fungus resistance | Non-nutrient | |
Note: The application and performance property values above are typical for the material, but not intended for use in specifications or for acceptance inspection criteria because of variations in testing methods, conditions and configurations.
Surface preparationImmediately before applying sealant to primed substrates, the surfaces should be cleaned with solvents. Contaminants such as dirt, grease, and/or processing lubricants must be removed prior to sealant application.
A progressive cleaning procedure should be employed using the appropriate solvents and new lint free cloth (reclaimed solvents or tissue paper should not be used). Always pour solvent on the cloth to avoid contaminating the solvent supply. Wash one small area at a time.
It is important that the surface is dried with a second clean cloth prior to the solvent evaporating to prevent the redeposition of contaminants on the substrate. Substrate composition can vary greatly. This can affect sealant adhesion. It is recommended that adhesion characteristics to a specific substrate be determined prior to application on production parts or assemblies.
For a more thorough discussion of proper surface preparation, please consult the SAE Aerospace Information Report AIR 4069. This document is available through SAE, 400 Commonwealth Avenue, Warrendale, PA 15096-0001.
Mixing instructions
PR-1425 Class B is supplied in a two-part kit. Mix according to the ratios indicated in the application properties section. Mix Part A and Part B separately to uniformity, then thoroughly mix entire contents of both parts of the kit to-gether taking care to avoid leaving unmixed areas around the sides or bottom of the mixing container.
Storage life
The storage life of PR-1425 Class B is at least 9 months when stored at temperatures between 40°F (5°C) and 80°F (27°C) in original unopened containers.
Health precautions
This product is safe to use and apply when recommended precautions are followed. Before using this product, read and understand the Material Safety Data Sheet (MSDS), which provides information on health, physical and environmental hazards, handling precautions and first aid recommendations. An MSDS is available on request. Avoid overexposure. Obtain medical care in case of extreme overexposure.
For industrial use only. Keep away from children.
For emergency medical information call 1-800-228-5635.