3M™ Aerospace AC-130-2 Clear BMS5-162 Type I, Form 2S Spec Surface Pre-Treatment - 50 mL Kit

3M™ Aerospace AC-130-2 Clear BMS5-162 Type I, Form 2S Spec Surface Pre-Treatment - 50 mL Kit
Our Part #: SGP5168
Manufacture Part #: 7000048184
Our Price: $73.39 (Each)

Bulk Shop & Save

  • 6 - 11 $72.30 (Each)
  • 12 - 23 $71.24 (Each)
  • 24 - 35 $70.21 (Each)
  • 36 + $69.21 (Each)
world wide icon INTERNATIONAL SHIPPING

SkyGeek welcomes international orders!

Please note: such orders are funneled into our NY warehouse and may take an extra 7-10 days to process. The benefit to this: You get one package shipped which reduces added taxes and duties that may be incurred from multiple shipments.

Related Items

Product Added to Cart Successfully

Approvals and Conformities

Approvals and Conformities

Boeing PN/Spec#
BMS5-162, Type I, Form 2S
Alternate PN#s
AC-130-2, AC130-2, 70-0052-0018-6, 70005200186, 051141-57819

Product Attributes

Country of Origin
United States
Size
50 mL
Shipping Weight
0.2 pounds
ECCN
EAR99
Color Family
Clear
Manufacturer P/N
7000048184
Schedule B Code
3214.10.0010
Pack Quantity
1
Ship Dimensions
6 x 5 x 1 inches
Size
50 mL Kit
Spec
BMS5-162 Type I, Form 2S
Color
Clear
A sol-gel surface preparation for adhesive bonding of aluminum alloys, steel and titanium. Promotes enhanced adhesion as a result of the chemical interaction at the interfaces between the metal, the AC-130-2 and the primer.
  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process
  • Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    • Features

  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    Downloads

    download icon Safety Data Sheet

    • Product Attributes

    Approvals and Conformities

    Boeing PN/Spec#
    BMS5-162, Type I, Form 2S
    Alternate PN#s
    AC-130-2, AC130-2, 70-0052-0018-6, 70005200186, 051141-57819

    Product Attributes

    Country of Origin
    United States
    Size
    50 mL
    Shipping Weight
    0.2 pounds
    ECCN
    EAR99
    Color Family
    Clear
    Manufacturer P/N
    7000048184
    Schedule B Code
    3214.10.0010
    Pack Quantity
    1
    Ship Dimensions
    6 x 5 x 1 inches
    Size
    50 mL Kit
    Spec
    BMS5-162 Type I, Form 2S
    Color
    Clear
    A sol-gel surface preparation for adhesive bonding of aluminum alloys, steel and titanium. Promotes enhanced adhesion as a result of the chemical interaction at the interfaces between the metal, the AC-130-2 and the primer.
  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process
  • Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    • Features

  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    Downloads

    download icon Safety Data Sheet

    • Description

    Approvals and Conformities

    Boeing PN/Spec#
    BMS5-162, Type I, Form 2S
    Alternate PN#s
    AC-130-2, AC130-2, 70-0052-0018-6, 70005200186, 051141-57819

    Product Attributes

    Country of Origin
    United States
    Size
    50 mL
    Shipping Weight
    0.2 pounds
    ECCN
    EAR99
    Color Family
    Clear
    Manufacturer P/N
    7000048184
    Schedule B Code
    3214.10.0010
    Pack Quantity
    1
    Ship Dimensions
    6 x 5 x 1 inches
    Size
    50 mL Kit
    Spec
    BMS5-162 Type I, Form 2S
    Color
    Clear
    A sol-gel surface preparation for adhesive bonding of aluminum alloys, steel and titanium. Promotes enhanced adhesion as a result of the chemical interaction at the interfaces between the metal, the AC-130-2 and the primer.
  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process
  • Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    • Features

  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    Downloads

    download icon Safety Data Sheet

    • Related Items

    Approvals and Conformities

    Approvals and Conformities

    Boeing PN/Spec#
    BMS5-162, Type I, Form 2S
    Alternate PN#s
    AC-130-2, AC130-2, 70-0052-0018-6, 70005200186, 051141-57819

    Product Attributes

    Country of Origin
    United States
    Size
    50 mL
    Shipping Weight
    0.2 pounds
    ECCN
    EAR99
    Color Family
    Clear
    Manufacturer P/N
    7000048184
    Schedule B Code
    3214.10.0010
    Pack Quantity
    1
    Ship Dimensions
    6 x 5 x 1 inches
    Size
    50 mL Kit
    Spec
    BMS5-162 Type I, Form 2S
    Color
    Clear
    A sol-gel surface preparation for adhesive bonding of aluminum alloys, steel and titanium. Promotes enhanced adhesion as a result of the chemical interaction at the interfaces between the metal, the AC-130-2 and the primer.
  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process
  • Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    • Features

  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    Downloads

    download icon Safety Data Sheet

    • Product Attributes

    Approvals and Conformities

    Boeing PN/Spec#
    BMS5-162, Type I, Form 2S
    Alternate PN#s
    AC-130-2, AC130-2, 70-0052-0018-6, 70005200186, 051141-57819

    Product Attributes

    Country of Origin
    United States
    Size
    50 mL
    Shipping Weight
    0.2 pounds
    ECCN
    EAR99
    Color Family
    Clear
    Manufacturer P/N
    7000048184
    Schedule B Code
    3214.10.0010
    Pack Quantity
    1
    Ship Dimensions
    6 x 5 x 1 inches
    Size
    50 mL Kit
    Spec
    BMS5-162 Type I, Form 2S
    Color
    Clear
    A sol-gel surface preparation for adhesive bonding of aluminum alloys, steel and titanium. Promotes enhanced adhesion as a result of the chemical interaction at the interfaces between the metal, the AC-130-2 and the primer.
  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process
  • Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    • Features

  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    Downloads

    download icon Safety Data Sheet

    • Description

    Approvals and Conformities

    Boeing PN/Spec#
    BMS5-162, Type I, Form 2S
    Alternate PN#s
    AC-130-2, AC130-2, 70-0052-0018-6, 70005200186, 051141-57819

    Product Attributes

    Country of Origin
    United States
    Size
    50 mL
    Shipping Weight
    0.2 pounds
    ECCN
    EAR99
    Color Family
    Clear
    Manufacturer P/N
    7000048184
    Schedule B Code
    3214.10.0010
    Pack Quantity
    1
    Ship Dimensions
    6 x 5 x 1 inches
    Size
    50 mL Kit
    Spec
    BMS5-162 Type I, Form 2S
    Color
    Clear
    A sol-gel surface preparation for adhesive bonding of aluminum alloys, steel and titanium. Promotes enhanced adhesion as a result of the chemical interaction at the interfaces between the metal, the AC-130-2 and the primer.
  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process
  • Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    • Features

  • Helps improve process efficiency; enables many metallic substances to be prepared with a single method
  • Up to 35% reduction in labor-time vs. PAA process; minimizes process flow time over Grit Blast Silane, PACS (tm) and PANTA (tm)
  • Helps minimize Aircraft on Ground (AOG) time compared to traditional processes; ambient-temperature curing allows for field repairs
  • Compatible with existing application techniques; brush, spray, wipe or dip application available
  • Comparable mechanical results to surfaces prepared with the PAA process Reduction in process flow time yields a minimum of a 35% reduction in labor time.

    Downloads

    download icon Safety Data Sheet