This 2.8 lb/gal VOC compliant, epoxy polyamide primer meets MIL-PRF-23377J, Class C2 composition and performance specification. It is used as a primer under MIL-PRF-85285 polyurethane topcoats.
This product has been qualified by the U.S. Naval Air Warfare Center (NAWC) Patuxent River, MD to MIL-PRF-23377J, Type I, Class C2.
2.8 lb/gal VOC.
Excellent chemical, solvent and corrosion resistance.
For aluminum with chromate Conversion coating or anodized aluminum, it offers excellent filiform resistance.
Features
2.8 lb/gal VOC
Fast drying
Excellent chemical, solvent and corrosion resistance
For aluminum with chromate conversion coating or anodized aluminum, it offers excellent filiform resistance
Excellent hold out for high gloss topcoats
Characteristics
Gloss
10-20 (60°)
Volume Solids
45% Catalyzed
Viscosity, 25 seconds (max.) #2 Zahn Cup
Catalyzed
Recommended Film Thickness Mils Wet Mils Dry
1.3-2.0 0.6-0.9
Spreading Rate (no application loss)
802-1203 sq ft/gal @ 0.6-0.9 mils DFT
Drying (0.8 mils dft, 77°F, 50% RH) Tack Free Dry Hard To Recoat Force Dry
5 hours 8 hours 2 hours To dry hard, 45-60 minutes at 140°F
Flash Point
22°F Pensky-Martens Closed Cup
Mixing Ratio (by volume) 3 parts 1 part
E90G203 or E90G205 V93V230
Induction Time
30 minutes
Pot Life
4 hours at room temperature. Higher temperature will shorten pot life
Aluminum: Clean with acidic cleaner or other appropriate cleaner depending on contamination. Pretreat with chromate conversion coating MIL-DTL-5541F, wash primer DOD-P-15328D, E90G4, or anodize per MIL-A-8625F.
Testing: Due to the wide variety of substrates, surface preparation methods, application methods, and environments, the customer should test the complete system for adhesion and compatibility prior to full scale application.
Product Limitations:
This product must be properly mixed (catalyzed) before using.
Surface preparation is important for performance.
For good adhesion, parts primed need to air dry a minimum of 2 hours before topcoating. If parts have been primed for longer than three days, they must be sanded or recoated with a mist coat before topcoating for good adhesion.