Guard your aircraft's sensitive surfaces against the common causes of corrosion by choosing PPG Aerospace® P/S 870 C-24 Corrosion Inhibiting Sealant from SkyGeek. The gray MIL-PRF-81733D Type IV-24 Class 1 GA Spec sealant consists of two components and is sold in a pre-measured kit with enough material to make 1 pint of sealant. The sealant has a service temperature range of -65ºF (-54ºC) to 250ºF (121ºC), with intermittent excursions up to 275ºF (135ºC), making it the ideal choice for most environments. When applied correctly, the material acts as a physical barrier against the common causes of corrosion on aluminum alloys, like moisture and aviation chemicals. The sealant maintains its elastomeric properties after limited exposure to jet fuel and aviation gas, making it the ideal choice for use all over the aircraft.
PPG Aerospace® P/S 870 C-24 Corrosion Inhibiting Sealant goes on smoothly and has a paste-like consistency for easy application on non-flat surfaces. Apply the sealant using an extrusion gun or spatula and smooth it into place. Once in position, the sealant will cure at room temperature into an impenetrable barrier. PPG Aerospace® P/S 870 C-24 Corrosion Inhibiting Sealant bonds well to most types of common aircraft substrates.
| Application Properties (typical) | | | Color | Part A - Black
Part B - White
Mixed - Gray | | Mixing ratio by weight | Part A: Part B
17:100 | | Base Viscosity | 2,500, (250)
(Brookfield #6 @ 10rpm), Poise (Pa-s) | Application life and cure time
@ 77°F (25°C), 50% RH | | | Application life (hours) | Tack free time (hours) | Cure time to 30 A Durometer (days) | | C-12 | 12 | 20 | 14 | | C-24 | 24 | 80 | 21 | | C-48 | 48 | 168 | 56 | | |
| Performance Properties (typical) | | | Cure Time | Cured in accordance with MIL-S-81733 Type IV | | Cured specific gravity | 1.50 | | Nonvolatile content,(%) | 90% | | Ultimate cure hardness (Durometer A) | 50 | | Peel strength, pli (N/25 mm),100% cohesion | | JP-4 fluid immersion, 2 days @ 140°F (60°C) | 3% fuel/NaCl-H2O immersion, 2 days @ 140°F (60°C) | | MIL-A-8625 (Anodized aluminum) - 21 (93) | MIL-A-8625 (Anodized aluminum) - 25 (111) | | MIL-T-9046 (Titanium comp. C)* - 26 (116) | MIL-T-9046 (Titanium comp. C)* - 26 (116) | | *Primed with PR-148 Adhesion Promoter | | | Tensile strength, psi (KPa) | 250 (1724) - Standard cure,14 days @77°F(25°C), 50% RH | | Elongation, % | 250 - Standard cure,14 days @77°F(25°C), 50% RH | | Soluble chromate, % | 4 | | Low temperature flexibility @ -65°F (-54°C) | No cracking, checking or loss of adhesion. | | Resistance to hydrocarbons | Weight loss : 7.0% - 7 days @ 140°F(60°C) immersed in Type III fuel. | | Flexibility | No cracks after bending 180 degrees over 0.125 inch (3.18 mm) mandrel. | | Repairability to itself | Excellent to both freshly cured as well as fuel aged and abraded fillets. | | Salt spray (fog) test for 1000 hrs. (ASTM B117) | No corrosion to base substrate or deterioration of sealant. | | Fungus resistance | Non-nutrient | |
Note: The application and performance property values above are typical for the material, but not intended for use in specifications or for acceptance inspection criteria because of variations in testing methods, conditions and configurations.
Surface preparationImmediately before applying sealant to primed substrates, the surfaces should be cleaned with solvents. Contaminants such as dirt, grease, and/or processing lubricants must be removed prior to sealant application.
A progressive cleaning procedure should be employed using the appropriate solvents and new lint free cloth (reclaimed solvents or tissue paper should not be used). Always pour solvent on the cloth to avoid contaminating the solvent supply. Wash one small area at a time.
It is important that the surface is dried with a second clean cloth prior to the solvent evaporating to prevent the redeposition of contaminants on the substrate.
Substrate composition can vary greatly. This can affect sealant adhesion. It is recommended that adhesion characteristics to a specific substrate be determined prior to application on production parts or assemblies.
For a more thorough discussion of proper surface preparation, please consult the SAE Aerospace Information Report AIR 4069. This document is available through SAE, 400 Commonwealth Avenue, Warrendale, PA 15096-0001.
Mixing instructions
P/S 870 Class C is supplied in a two-part kit. Mix according to the ratios indicated in the application properties section. Mix Part A and Part B separately to uniformity, then thoroughly mix entire contents of both parts of the kit together taking care to avoid leaving unmixed areas around the sides or bottom of the mixing container.
Storage life
The storage life of P/S 870 Class C is at least 6 months when stored at temperatures below 80°F (27°C) in original unopened containers.
Health precautions
This product is safe to use and apply when recommended precautions are followed. Before using this product, read and understand the Material Safety Data Sheet (MSDS), which provides information on health, physical and environmental hazards, handling precautions and first aid recommendations. An MSDS is available on request. Avoid overexposure. Obtain medical care in case of extreme overexposure.
For industrial use only. Keep away from children.
For emergency medical information call 1-800-228-5635.
Safety Data Sheet