Flamemaster CS-3204 B-2 Gray AMS-S-8802E Type 2 Spec Integral Fuel Tank Sealant - Quart (24 fl oz) Can Kit

Our Part #: SGP106605
Manufacture Part #: CS3204B2-GRY-QT
Our Price: $65.06 (Each)

Bulk Shop & Save

  • 12 - 23 $64.17 (Each)
  • 24 - 35 $63.30 (Each)
  • 36 - 47 $62.46 (Each)
  • 48 + $61.64 (Each)
world wide icon INTERNATIONAL SHIPPING

SkyGeek welcomes international orders!

Please note: such orders are funneled into our NY warehouse and may take an extra 7-10 days to process. The benefit to this: You get one package shipped which reduces added taxes and duties that may be incurred from multiple shipments.

Approvals and Conformities

Approvals and Conformities

SAE Spec#
AMS-S-8802 Rev. E Type 2

Product Attributes

Country of Origin
United States
Size
Quart
Shipping Weight
3.5 pounds
ECCN
EAR99
Color Family
Gray
Manufacturer P/N
CS-3204 Class B-2
Schedule B Code
3506.91.0000
Pack Quantity
1
Ship Dimensions
4 x 4 x 7 inches
Size
Quart (24 fl oz) Can Kit
Spec
AMS-S-8802E Type 2
Class
B-2
Color
Gray
Integral Fuel Tank Sealant Designed to withstand the attack of sulfur compounds present in jet fuels. Also used as pressurized cabin sealant.

Features

Typical Properties MIS-31868C CS 3204 WT20
Color:
Base Compound Aluminum
Curing Agent Black
Mixed Aluminum
Mixing Ratio:
Weight 7.8/10:100 10/100
Volume N/A 8.3/100
Non Volatile 75% 80%
Viscosity Mixed 100-180 PS.a 116 PS.a

Homogeneity

11.4% ± 2% 12.5%
Extrudability Extrudable Pass
Application Life 5 grams min. 90 grams
Squeeze Out Hardness (Shore A) N/A

20 hours

120 Hrs. @24C ± 1C 35 (min.)

50 (min.)

28 days @24C ± 1C 50 (min.) 60 (min.)
Shelf Life @ 28C± 1C 6 months 6 months
Flash Point N/A + 15C

SURFACE PREPARATION

To obtain good adhesion, remove all traces of oil, wax, grease, dirt, or other contamination. Working in small area segments, wipe the surface using a clean rag doused in an oil free solvent. Before the solvent evaporates, wipe the surface dry with a second clean rag. Maintain a clean solvent supply by pouring the solvent on the washing cloth. CS 3204 will adhere tenaciously to most substrates providing the surface to be sealed is clean and sound.

MIXING INSTRUCTIONS

CS 3204 Parts A and B are carefully matched at the time of manufacture to provide optimum performance when cured. Care should be taken to assure that Parts A and B are combined as recommended on the container label. When mixing pre-measured kits do not thin CS 3204 with solvents. Prior to combining with the Part A component, stir the Part B component until the contents of the container are uniform. Place all of the B component into the Part A container and continue stirring until a uniform gray color is achieved. There should be no white or black streaks in the properly blended material. Periodically scrape the sides and bottom of the container as well as the mixing tool to assure proper mixing. When using a mechanical mixer, avoid high speeds since the heat generated will reduce the application time of the mixed CS 3204. Violent stirring will also entrap air in the cured sealant.

When mixing materials packaged in bulk or when only a small quantity is required, stir 10 parts by weight of the Part B component into 100 parts by weight of the Part A component. Be sure to stir the Part B prior to weighing out the required amount.

CURE

Specified application and cure schedules are based on the standard conditions of 77°F and 50% relative humidity. Increased temperature and relative humidity will reduce the work life and speed up the cure while reduced temperatures and relative humidity will extend the work life and slow the cure. Cure may be accelerated by heating up to 120°F. However care must be exercised to avoid the entrapment of solvent when heat is applied.

Downloads

download icon Safety Data Sheet

Product Attributes

Approvals and Conformities

SAE Spec#
AMS-S-8802 Rev. E Type 2

Product Attributes

Country of Origin
United States
Size
Quart
Shipping Weight
3.5 pounds
ECCN
EAR99
Color Family
Gray
Manufacturer P/N
CS-3204 Class B-2
Schedule B Code
3506.91.0000
Pack Quantity
1
Ship Dimensions
4 x 4 x 7 inches
Size
Quart (24 fl oz) Can Kit
Spec
AMS-S-8802E Type 2
Class
B-2
Color
Gray
Integral Fuel Tank Sealant Designed to withstand the attack of sulfur compounds present in jet fuels. Also used as pressurized cabin sealant.

Features

Typical Properties MIS-31868C CS 3204 WT20
Color:
Base Compound Aluminum
Curing Agent Black
Mixed Aluminum
Mixing Ratio:
Weight 7.8/10:100 10/100
Volume N/A 8.3/100
Non Volatile 75% 80%
Viscosity Mixed 100-180 PS.a 116 PS.a

Homogeneity

11.4% ± 2% 12.5%
Extrudability Extrudable Pass
Application Life 5 grams min. 90 grams
Squeeze Out Hardness (Shore A) N/A

20 hours

120 Hrs. @24C ± 1C 35 (min.)

50 (min.)

28 days @24C ± 1C 50 (min.) 60 (min.)
Shelf Life @ 28C± 1C 6 months 6 months
Flash Point N/A + 15C

SURFACE PREPARATION

To obtain good adhesion, remove all traces of oil, wax, grease, dirt, or other contamination. Working in small area segments, wipe the surface using a clean rag doused in an oil free solvent. Before the solvent evaporates, wipe the surface dry with a second clean rag. Maintain a clean solvent supply by pouring the solvent on the washing cloth. CS 3204 will adhere tenaciously to most substrates providing the surface to be sealed is clean and sound.

MIXING INSTRUCTIONS

CS 3204 Parts A and B are carefully matched at the time of manufacture to provide optimum performance when cured. Care should be taken to assure that Parts A and B are combined as recommended on the container label. When mixing pre-measured kits do not thin CS 3204 with solvents. Prior to combining with the Part A component, stir the Part B component until the contents of the container are uniform. Place all of the B component into the Part A container and continue stirring until a uniform gray color is achieved. There should be no white or black streaks in the properly blended material. Periodically scrape the sides and bottom of the container as well as the mixing tool to assure proper mixing. When using a mechanical mixer, avoid high speeds since the heat generated will reduce the application time of the mixed CS 3204. Violent stirring will also entrap air in the cured sealant.

When mixing materials packaged in bulk or when only a small quantity is required, stir 10 parts by weight of the Part B component into 100 parts by weight of the Part A component. Be sure to stir the Part B prior to weighing out the required amount.

CURE

Specified application and cure schedules are based on the standard conditions of 77°F and 50% relative humidity. Increased temperature and relative humidity will reduce the work life and speed up the cure while reduced temperatures and relative humidity will extend the work life and slow the cure. Cure may be accelerated by heating up to 120°F. However care must be exercised to avoid the entrapment of solvent when heat is applied.

Downloads

download icon Safety Data Sheet

Description

Approvals and Conformities

SAE Spec#
AMS-S-8802 Rev. E Type 2

Product Attributes

Country of Origin
United States
Size
Quart
Shipping Weight
3.5 pounds
ECCN
EAR99
Color Family
Gray
Manufacturer P/N
CS-3204 Class B-2
Schedule B Code
3506.91.0000
Pack Quantity
1
Ship Dimensions
4 x 4 x 7 inches
Size
Quart (24 fl oz) Can Kit
Spec
AMS-S-8802E Type 2
Class
B-2
Color
Gray
Integral Fuel Tank Sealant Designed to withstand the attack of sulfur compounds present in jet fuels. Also used as pressurized cabin sealant.

Features

Typical Properties MIS-31868C CS 3204 WT20
Color:
Base Compound Aluminum
Curing Agent Black
Mixed Aluminum
Mixing Ratio:
Weight 7.8/10:100 10/100
Volume N/A 8.3/100
Non Volatile 75% 80%
Viscosity Mixed 100-180 PS.a 116 PS.a

Homogeneity

11.4% ± 2% 12.5%
Extrudability Extrudable Pass
Application Life 5 grams min. 90 grams
Squeeze Out Hardness (Shore A) N/A

20 hours

120 Hrs. @24C ± 1C 35 (min.)

50 (min.)

28 days @24C ± 1C 50 (min.) 60 (min.)
Shelf Life @ 28C± 1C 6 months 6 months
Flash Point N/A + 15C

SURFACE PREPARATION

To obtain good adhesion, remove all traces of oil, wax, grease, dirt, or other contamination. Working in small area segments, wipe the surface using a clean rag doused in an oil free solvent. Before the solvent evaporates, wipe the surface dry with a second clean rag. Maintain a clean solvent supply by pouring the solvent on the washing cloth. CS 3204 will adhere tenaciously to most substrates providing the surface to be sealed is clean and sound.

MIXING INSTRUCTIONS

CS 3204 Parts A and B are carefully matched at the time of manufacture to provide optimum performance when cured. Care should be taken to assure that Parts A and B are combined as recommended on the container label. When mixing pre-measured kits do not thin CS 3204 with solvents. Prior to combining with the Part A component, stir the Part B component until the contents of the container are uniform. Place all of the B component into the Part A container and continue stirring until a uniform gray color is achieved. There should be no white or black streaks in the properly blended material. Periodically scrape the sides and bottom of the container as well as the mixing tool to assure proper mixing. When using a mechanical mixer, avoid high speeds since the heat generated will reduce the application time of the mixed CS 3204. Violent stirring will also entrap air in the cured sealant.

When mixing materials packaged in bulk or when only a small quantity is required, stir 10 parts by weight of the Part B component into 100 parts by weight of the Part A component. Be sure to stir the Part B prior to weighing out the required amount.

CURE

Specified application and cure schedules are based on the standard conditions of 77°F and 50% relative humidity. Increased temperature and relative humidity will reduce the work life and speed up the cure while reduced temperatures and relative humidity will extend the work life and slow the cure. Cure may be accelerated by heating up to 120°F. However care must be exercised to avoid the entrapment of solvent when heat is applied.

Downloads

download icon Safety Data Sheet

Approvals and Conformities

Approvals and Conformities

SAE Spec#
AMS-S-8802 Rev. E Type 2

Product Attributes

Country of Origin
United States
Size
Quart
Shipping Weight
3.5 pounds
ECCN
EAR99
Color Family
Gray
Manufacturer P/N
CS-3204 Class B-2
Schedule B Code
3506.91.0000
Pack Quantity
1
Ship Dimensions
4 x 4 x 7 inches
Size
Quart (24 fl oz) Can Kit
Spec
AMS-S-8802E Type 2
Class
B-2
Color
Gray
Integral Fuel Tank Sealant Designed to withstand the attack of sulfur compounds present in jet fuels. Also used as pressurized cabin sealant.

Features

Typical Properties MIS-31868C CS 3204 WT20
Color:
Base Compound Aluminum
Curing Agent Black
Mixed Aluminum
Mixing Ratio:
Weight 7.8/10:100 10/100
Volume N/A 8.3/100
Non Volatile 75% 80%
Viscosity Mixed 100-180 PS.a 116 PS.a

Homogeneity

11.4% ± 2% 12.5%
Extrudability Extrudable Pass
Application Life 5 grams min. 90 grams
Squeeze Out Hardness (Shore A) N/A

20 hours

120 Hrs. @24C ± 1C 35 (min.)

50 (min.)

28 days @24C ± 1C 50 (min.) 60 (min.)
Shelf Life @ 28C± 1C 6 months 6 months
Flash Point N/A + 15C

SURFACE PREPARATION

To obtain good adhesion, remove all traces of oil, wax, grease, dirt, or other contamination. Working in small area segments, wipe the surface using a clean rag doused in an oil free solvent. Before the solvent evaporates, wipe the surface dry with a second clean rag. Maintain a clean solvent supply by pouring the solvent on the washing cloth. CS 3204 will adhere tenaciously to most substrates providing the surface to be sealed is clean and sound.

MIXING INSTRUCTIONS

CS 3204 Parts A and B are carefully matched at the time of manufacture to provide optimum performance when cured. Care should be taken to assure that Parts A and B are combined as recommended on the container label. When mixing pre-measured kits do not thin CS 3204 with solvents. Prior to combining with the Part A component, stir the Part B component until the contents of the container are uniform. Place all of the B component into the Part A container and continue stirring until a uniform gray color is achieved. There should be no white or black streaks in the properly blended material. Periodically scrape the sides and bottom of the container as well as the mixing tool to assure proper mixing. When using a mechanical mixer, avoid high speeds since the heat generated will reduce the application time of the mixed CS 3204. Violent stirring will also entrap air in the cured sealant.

When mixing materials packaged in bulk or when only a small quantity is required, stir 10 parts by weight of the Part B component into 100 parts by weight of the Part A component. Be sure to stir the Part B prior to weighing out the required amount.

CURE

Specified application and cure schedules are based on the standard conditions of 77°F and 50% relative humidity. Increased temperature and relative humidity will reduce the work life and speed up the cure while reduced temperatures and relative humidity will extend the work life and slow the cure. Cure may be accelerated by heating up to 120°F. However care must be exercised to avoid the entrapment of solvent when heat is applied.

Downloads

download icon Safety Data Sheet

Product Attributes

Approvals and Conformities

SAE Spec#
AMS-S-8802 Rev. E Type 2

Product Attributes

Country of Origin
United States
Size
Quart
Shipping Weight
3.5 pounds
ECCN
EAR99
Color Family
Gray
Manufacturer P/N
CS-3204 Class B-2
Schedule B Code
3506.91.0000
Pack Quantity
1
Ship Dimensions
4 x 4 x 7 inches
Size
Quart (24 fl oz) Can Kit
Spec
AMS-S-8802E Type 2
Class
B-2
Color
Gray
Integral Fuel Tank Sealant Designed to withstand the attack of sulfur compounds present in jet fuels. Also used as pressurized cabin sealant.

Features

Typical Properties MIS-31868C CS 3204 WT20
Color:
Base Compound Aluminum
Curing Agent Black
Mixed Aluminum
Mixing Ratio:
Weight 7.8/10:100 10/100
Volume N/A 8.3/100
Non Volatile 75% 80%
Viscosity Mixed 100-180 PS.a 116 PS.a

Homogeneity

11.4% ± 2% 12.5%
Extrudability Extrudable Pass
Application Life 5 grams min. 90 grams
Squeeze Out Hardness (Shore A) N/A

20 hours

120 Hrs. @24C ± 1C 35 (min.)

50 (min.)

28 days @24C ± 1C 50 (min.) 60 (min.)
Shelf Life @ 28C± 1C 6 months 6 months
Flash Point N/A + 15C

SURFACE PREPARATION

To obtain good adhesion, remove all traces of oil, wax, grease, dirt, or other contamination. Working in small area segments, wipe the surface using a clean rag doused in an oil free solvent. Before the solvent evaporates, wipe the surface dry with a second clean rag. Maintain a clean solvent supply by pouring the solvent on the washing cloth. CS 3204 will adhere tenaciously to most substrates providing the surface to be sealed is clean and sound.

MIXING INSTRUCTIONS

CS 3204 Parts A and B are carefully matched at the time of manufacture to provide optimum performance when cured. Care should be taken to assure that Parts A and B are combined as recommended on the container label. When mixing pre-measured kits do not thin CS 3204 with solvents. Prior to combining with the Part A component, stir the Part B component until the contents of the container are uniform. Place all of the B component into the Part A container and continue stirring until a uniform gray color is achieved. There should be no white or black streaks in the properly blended material. Periodically scrape the sides and bottom of the container as well as the mixing tool to assure proper mixing. When using a mechanical mixer, avoid high speeds since the heat generated will reduce the application time of the mixed CS 3204. Violent stirring will also entrap air in the cured sealant.

When mixing materials packaged in bulk or when only a small quantity is required, stir 10 parts by weight of the Part B component into 100 parts by weight of the Part A component. Be sure to stir the Part B prior to weighing out the required amount.

CURE

Specified application and cure schedules are based on the standard conditions of 77°F and 50% relative humidity. Increased temperature and relative humidity will reduce the work life and speed up the cure while reduced temperatures and relative humidity will extend the work life and slow the cure. Cure may be accelerated by heating up to 120°F. However care must be exercised to avoid the entrapment of solvent when heat is applied.

Downloads

download icon Safety Data Sheet

Description

Approvals and Conformities

SAE Spec#
AMS-S-8802 Rev. E Type 2

Product Attributes

Country of Origin
United States
Size
Quart
Shipping Weight
3.5 pounds
ECCN
EAR99
Color Family
Gray
Manufacturer P/N
CS-3204 Class B-2
Schedule B Code
3506.91.0000
Pack Quantity
1
Ship Dimensions
4 x 4 x 7 inches
Size
Quart (24 fl oz) Can Kit
Spec
AMS-S-8802E Type 2
Class
B-2
Color
Gray
Integral Fuel Tank Sealant Designed to withstand the attack of sulfur compounds present in jet fuels. Also used as pressurized cabin sealant.

Features

Typical Properties MIS-31868C CS 3204 WT20
Color:
Base Compound Aluminum
Curing Agent Black
Mixed Aluminum
Mixing Ratio:
Weight 7.8/10:100 10/100
Volume N/A 8.3/100
Non Volatile 75% 80%
Viscosity Mixed 100-180 PS.a 116 PS.a

Homogeneity

11.4% ± 2% 12.5%
Extrudability Extrudable Pass
Application Life 5 grams min. 90 grams
Squeeze Out Hardness (Shore A) N/A

20 hours

120 Hrs. @24C ± 1C 35 (min.)

50 (min.)

28 days @24C ± 1C 50 (min.) 60 (min.)
Shelf Life @ 28C± 1C 6 months 6 months
Flash Point N/A + 15C

SURFACE PREPARATION

To obtain good adhesion, remove all traces of oil, wax, grease, dirt, or other contamination. Working in small area segments, wipe the surface using a clean rag doused in an oil free solvent. Before the solvent evaporates, wipe the surface dry with a second clean rag. Maintain a clean solvent supply by pouring the solvent on the washing cloth. CS 3204 will adhere tenaciously to most substrates providing the surface to be sealed is clean and sound.

MIXING INSTRUCTIONS

CS 3204 Parts A and B are carefully matched at the time of manufacture to provide optimum performance when cured. Care should be taken to assure that Parts A and B are combined as recommended on the container label. When mixing pre-measured kits do not thin CS 3204 with solvents. Prior to combining with the Part A component, stir the Part B component until the contents of the container are uniform. Place all of the B component into the Part A container and continue stirring until a uniform gray color is achieved. There should be no white or black streaks in the properly blended material. Periodically scrape the sides and bottom of the container as well as the mixing tool to assure proper mixing. When using a mechanical mixer, avoid high speeds since the heat generated will reduce the application time of the mixed CS 3204. Violent stirring will also entrap air in the cured sealant.

When mixing materials packaged in bulk or when only a small quantity is required, stir 10 parts by weight of the Part B component into 100 parts by weight of the Part A component. Be sure to stir the Part B prior to weighing out the required amount.

CURE

Specified application and cure schedules are based on the standard conditions of 77°F and 50% relative humidity. Increased temperature and relative humidity will reduce the work life and speed up the cure while reduced temperatures and relative humidity will extend the work life and slow the cure. Cure may be accelerated by heating up to 120°F. However care must be exercised to avoid the entrapment of solvent when heat is applied.